HTD,STS,RPP & DD

 

H3M      

Standard compound: Polyurethane 92 ShA
Standard width tolerance: +/-0,3 mm  
Standard thickness: 2,2 +/-0,15 mm
Standard length tolerance: +/-0,8 mm/m  
Standard roll length: 100 m  
         
  STANDARD WIDTHS (inch) 10 20 25 50  
  Weight (gr/m)   20 45 60 115  
  Steel Max Traction Load (N) 385 775 1010 2060  
Breaking Strength (N) 1555 3115 4050 8255  
Elongation at MTL (mm/m) 4 4 4 4  

 

H5M      

Standard compound: Polyurethane 92 ShA
Standard width tolerance: +/-0,5 mm  
Standard thickness: 3,6 +/-0,2 mm
Standard length tolerance: +/-0,8 mm/m  
Standard roll length: 100 m  
         
  STANDARD WIDTHS (inch) 10 15 25 50  
  Weight (gr/m)   35 50 80 165  
  Steel Max Traction Load (N) 635 950 1715 3560  
Breaking Strength (N) 2545 3815 6870 14255  
Elongation at MTL (mm/m) 4 4 4 4  
  Kevlar Max Traction Load (N) 665 995 1795 3720  
Breaking Strength (N) 2660 3990 7180 14895  
Elongation at MTL (mm/m) 8 8 8 8  
  Stainless  Max Traction Load (N) 520 780 1410 -   
Breaking Strength (N) 2090 3135 5640 -   
Elongation at MTL (mm/m) 3,8 3,8 3,8 -   

 

H8M      

Standard compound: Polyurethane 92 ShA
Standard width tolerance: +/-0,5 mm  
Standard thickness: 5,6 +/-0,3 mm
Standard length tolerance: +/-0,8 mm/m
Standard roll length: 100 m  
         
  STANDARD WIDTHS (inch) 10 15 20 30 50 85 100  
  Weight (gr/m)   65 85 120 185 325 530 650  
  Steel Max Traction Load (N) 1350 2030 2930 4510 7670 14010 16625  
Breaking Strength (N) 5415 8120 11730 18050 30685 53245 63175  
Elongation at MTL (mm/m) 5 5 5 5 5 5 5  
  Kevlar Max Traction Load (N) 765 1150 1535 2565 4360 7965 9450  
Breaking Strength (N) 3075 4615 6155 10260 17440 30265 35910  
Elongation at MTL (mm/m) 8 8 8 8 8 8 8  
  Stainless  Max Traction Load (N) 1075 1610 2330 3585 6095 - -  
Breaking Strength (N) 4300 6455 9320 14345 24385 - -  
Elongation at MTL (mm/m) 3,8 3,8 3,8 3,8 3,8 -